5791C90003
& 5791C90003A
MC Replacement GS-3 Mold Release
Product
Description
5791C90003 is a dry lubricant composed of a dispersion of fluorocarbon
particles carried in methylene chloride and co-solvent rather than
ozone-depleting freon or 1,1,1, trichlorethane. 5791C90003 forms
a dry lubricant film and is primarily a release agent for polyesters,
epoxies and a wide variety of thermosetting resins.
5791C90003
is an excellent metal-to-metal lubricant for locks, machinery, conveyers,
drawer glides and wood or metal working equipment.
5791C90003A
is the Aerosol version of GS-3.
Typical
Physical Characteristics (All Tests at 77º
F.)
| Weight
Per Gallon: |
11.2 pounds
|
| Flash
Point: |
Greater than 185° Fahrenheit
|
| DOT
Classification: |
Not
flammable |
| VOC
(EPA Method 24): |
0
grams/liter |
| Shelf
Life: |
One
year from date of shipment |
|
|
Application
5791C90003
is best applied by spray gun or wiping on a heated mold with a clean
cloth for an even coating. Shake well before using and during prolonged
applications, as the settling rate is fairly rapid. Allow to dry
completely - elevated temperature will speed the evaporation of
solvent. Buff lightly to develop the slick surface desired.
The
sprayed particles can also be flame fused to a continuous coating
by playing a burner flame lightly and repeatedly over the treated
surface (melting point is approximately 570° F.). Care should
be taken that the surface is not burned while heat-treating. Use
adequate ventilation when flame fusing to prevent fume fever.
|